Effect of creep loading on the oxygen diffusion of Ti6242S at 650°C

Résumé

The influence of low and steady loading on the oxidation behaviour and oxygen diffusion within Ti6242S was investigated at 650 °C in air. Electron probe microanalyser (EPMA), secondary-ion mass spectrometry (SIMS) and high energy synchrotron X-ray diffraction (S-XRD) were used to quantify the oxygen distribution within the oxygen-enriched layer beneath the external oxide scale. Rietveld and peak by peak methods were used to evaluate the average response versus the crystal-oriented response of this diffusion process under load. Interestingly, a thermo-mechano-chemical coupling occurs during the creep-oxidation experiment even for moderate applied stresses (25-70 MPa) and demonstrates: (i) a decrease of the oxygen concentration at the metal/oxide interface, and (ii) a curvature change of the oxygen diffusion profile with load application. A qualitative thermo-mechano-chemical approach is proposed to model the modification of the diffusion law of the oxygen within Ti6242S due to application of a mechanical loading to explain observed experimental results.
Fichier principal
Vignette du fichier
Effect_creep-loading-oxygen-diffusion-Ti6242S.pdf (1.82 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04204533 , version 1 (13-09-2023)

Identifiants

Citer

K. Cavé, D. Texier, S. Vallot, N. Chanfreau, E. Fessler, et al.. Effect of creep loading on the oxygen diffusion of Ti6242S at 650°C. Scripta Materialia, 2024, 238, pp.115748. ⟨10.1016/j.scriptamat.2023.115748⟩. ⟨hal-04204533⟩
181 Consultations
7 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More