Strain localization in the Alloy 718 Ni-based superalloy: From room temperature to 650 °C - IMT Mines Albi-Carmaux Accéder directement au contenu
Article Dans Une Revue Acta Materialia Année : 2024

Strain localization in the Alloy 718 Ni-based superalloy: From room temperature to 650 °C

Résumé

Irreversible deformation in relation to the microstructure was investigated for a polycrystalline Ni-based superalloy (Alloy 718) from room temperature to 650 °C using high-resolution digital image correlation (HR-DIC) techniques. Interrupted tensile tests were performed under a protective atmosphere to ensure the stability of the speckle pattern to track kinematics fields from surface analyses. In-plane strain localization was captured using HR-DIC on scanning electron microscopy (SEM) images. A statistical analysis of different strain localization events in relation to the microstructural features was conducted, i.e., intragranular slip localization, slip localization parallel to and near Σ3-twin boundaries (Σ3-TB), and grain boundary sliding (GBS). Alloy 718 exhibited slip localization at room temperature and 350 °C. Intense strain localization develops parallel and in the vicinity of Σ3-TB from the onset of the microplasticity. Few intense slip stimulated-grain boundary sliding events were found due to slip localization on both grains adjacent to the grain boundary. At 650 °C, Alloy 718 experienced grain boundary sliding at the onset of the yield without particular slip localization in adjacent grains. At lower temperatures, strain localization parallel to and near Σ3-TB was intense, and intragranular slip localization intensified with increasing macroscopic deformation. Particular microstructural configurations were found at 650 °C leading to premature damage: (i) sub-surface cavitation at grain boundaries, and (ii) grain boundary cracking due to intense shearing near a Σ3-TB.
Fichier principal
Vignette du fichier
Strain_localization_in_the_Alloy_718.pdf (10.37 Mo) Télécharger le fichier
Origine : Publication financée par une institution
Licence : CC BY - Paternité

Dates et versions

hal-04457558 , version 1 (06-03-2024)

Licence

Paternité

Identifiants

Citer

Damien Texier, Julien Milanese, Malo Jullien, Julien Genee, Jean-Charles Passieux, et al.. Strain localization in the Alloy 718 Ni-based superalloy: From room temperature to 650 °C. Acta Materialia, 2024, 268, pp.119759. ⟨10.1016/j.actamat.2024.119759⟩. ⟨hal-04457558⟩
52 Consultations
9 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More