Co-pyrolysis of wood and plastics

(1) , (1) , (2) , (2) , (1) , (1)
1
2

Abstract

In recent years, the world has witnessed a rapid rise in waste production and energy demand, which has increased interests in waste to energy processes, particularly the co-pyrolysis of wood and plastic waste. Nonetheless, for plastic waste, most research studies narrowly focus on polyolefins because of their abundance in waste streams and their high oil yields from pyrolysis. In this paper, we study the co-pyrolysis of non-polyolefins – polystyrene (PS) and polyvinyl chloride (PVC) – and poplar wood (PW), in order to investigate the synergistic effect of PS and PVC content on product yield, gas specie yield and heating value. The experiments were performed using a fixed-bed reactor, heated to 750 °°C at a rate of 20 °°C/min under nitrogen atmosphere. Our results show that PVC has a large positive synergy on char yield with a maximum value of 8 wt% at 30 wt% PVC content, whereas PS only showed a slightly positive synergy (2.5 wt% maximum). Concerning oil and gas production, PS provides a small synergy. However, PVC showed a significant positive synergy on oil yield with a maximum value of 11 wt% at 50 wt% PVC content, which was linked to a strong negative synergy in gas production. Regarding gas specie yields, the addition of PS led to positive synergies in the formation of H2, CH4, CO and CO2, although insignificant interactions were observed for CxHyCxHy compounds. Furthermore, by comparing the distribution of chloride species in the products of co-pyrolysis with PVC, using experimental and theoretical methods, we discovered that the negative synergy in HCl yield observed was mainly due to the dissolution of HCl in the water fraction of the condensed oil phase, rather than the formation of chlorinated organic compounds, as suggested in previous literature works. Our study therefore consolidates the understanding of the synergistic interactions between wood, PS and PVC co-pyrolysis, under conditions that favour gas production.
Fichier principal
Vignette du fichier
co-pyrolysis-of-wood-and-plastics.pdf (1.53 Mo) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-01802140 , version 1 (20-10-2018)

Identifiers

Cite

Augustina Ephraim, Doan Pham Minh, Damien Lebonnois, Carlos Peregrina, Patrick Sharrock, et al.. Co-pyrolysis of wood and plastics: Influence of plastic type and content on product yield, gas composition and quality. Fuel, 2018, 231, p.110 - 117. ⟨10.1016/j.fuel.2018.04.140⟩. ⟨hal-01802140⟩
80 View
549 Download

Altmetric

Share

Gmail Facebook Twitter LinkedIn More