Improved aromatic yield and toluene selectivity in propane aromatization over Zn–Co/ZSM-5: effect of metal composition and process conditions - IMT Mines Albi-Carmaux Accéder directement au contenu
Article Dans Une Revue Journal of Porous Materials Année : 2023

Improved aromatic yield and toluene selectivity in propane aromatization over Zn–Co/ZSM-5: effect of metal composition and process conditions

Résumé

In this report, a catalytic enhanced-conventional process production background was employed to determine the most cost-effective and environmentally friendly techniques to improve the catalytic production of toluene and other aromatic compounds from propane aromatization. 2 wt% of zinc was co-impregnated with 1–3 wt% of cobalt on HZSM-5. Characterizations and analysis showed that catalysts are crystalline and microporous. Propane conversion was carried out at 540 °C, 1200 ml/g-h gas hourly space velocity and atmospheric pressure over Zn–Co/ZSM-5 bimetallic catalysts. Toluene selectivity in the aromatic products was greatly improved and sustained significantly together with other aromatic products. Catalytic conversion of propane and aromatic yield over Zn–Co/ZSM-5 was improved and stabilized due to metallic collaboration on HZSM-5. Aromatic yield averaged 46, 32, and 36%, respectively, for 1–3 wt% Co in Zn–Co/ZSM-5 bimetallic catalyst. Average toluene selectivity in the aromatic products for 12 h time on stream from 60, 50 and 51% for 1–3 wt% Co loading. The threshold loading of cobalt with zinc was 2% above which the general aromatic selectivity declined. A decrease in conversion from 73 to 15% was observed for flowrate increase from 6 to 35 ml min−1 and an increase in aromatic selectivity from 80 to 87%. An increase in temperature of 500–560 °C increased catalytic performance, 32–47% for propane conversion, and 79–86% aromatic selectivity.
Fichier principal
Vignette du fichier
Improved-aromatic-yield-and-toluene-selectivity-in-propane-aromatization-over-Zn-Co-ZSM-5-effect-of-metal-composition-and-process-conditions.pdf (965.31 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03882121 , version 1 (05-12-2022)

Identifiants

Citer

G. Oseke, E. Peter, A. Atta, B. Mukhtar, B. El-Yakubu, et al.. Improved aromatic yield and toluene selectivity in propane aromatization over Zn–Co/ZSM-5: effect of metal composition and process conditions. Journal of Porous Materials, 2023, 30, p. 999-1010. ⟨10.1007/s10934-022-01397-w⟩. ⟨hal-03882121⟩
124 Consultations
55 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More