Binary and ternary alkali polyphosphates (MPO3, M = Li, Na, K) for thermal energy storage - Archive ouverte HAL Access content directly
Journal Articles Journal of Thermal Analysis and Calorimetry Year : 2021

Binary and ternary alkali polyphosphates (MPO3, M = Li, Na, K) for thermal energy storage

(1, 2) , (3, 2) , (2) , (1) , (4) , (5) , (6) , (6) , (2) , (2)
1
2
3
4
5
6

Abstract

Up-to-date, solar salt (a mixture of 60 mass% NaNO3 and 40 mass% KNO3) is practically the only media for thermal energy storage (TES) in concentrated solar power (CSP). This commercial product’s utilization is limited below 550 °C to avoid an irreversible thermal decomposition. The development of new performing TES materials is decisive for the deployment of CSP technology. Our recent work reported promising results obtained with mono-alkali polyphosphate (M-PO3) as TES materials. These materials can work up to around 900 °C, but their melting point is still high, which is at least 628 °C. In order to lower their melting point, binary and ternary mixtures of alkali polyphosphates are investigated in this work. Dif- ferent mixtures made of two or three alkali polyphosphates were prepared and studied using thermal analysis methods. The most promising mixture found in this work was the ternary Li-Na-K-PO3, which contained 33.3% (mol%) of each alkali metal. This mixture can be used as a liquid TES material in the temperature range of 398 to 900 °C. The results open new prospects for the development of the thermal energy storage field.
Fichier principal
Vignette du fichier
Binary-and-ternary-alkali-polyphosphates-MPO3-M-Li-Na-K-for-thermal-energy-storage.pdf (1.01 Mo) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-03012742 , version 1 (20-11-2020)

Identifiers

Cite

Hieu Pham Sy, Doan Pham Minh, Abdoul Razac Sane, Hoan Nguyen Xuan, Nawal Semlal, et al.. Binary and ternary alkali polyphosphates (MPO3, M = Li, Na, K) for thermal energy storage. Journal of Thermal Analysis and Calorimetry, 2021, 146, pp.2027-2033. ⟨10.1007/s10973-020-10346-1⟩. ⟨hal-03012742⟩
92 View
79 Download

Altmetric

Share

Gmail Facebook Twitter LinkedIn More