Pyrolysis of wood at high temperature: The influence of experimental parameters on gaseous products

Résumé

The pyrolysis of wood was carried out in an Entrained Flow Reactor at high temperature (650 to 950 °C) and under rapid heating conditions (N 10 3 K s − 1). The influence of the diameter and initial moisture of the particle, reactor temperature, residence time and the nature of the gaseous atmosphere on the composition of the gaseous products has been characterised. Particle size, between 80–125 and 160–200 μm, did not show any impact. Pyrolysis and tar cracking essentially happen in very short time period: less than 0.6 s; the products yields are only slightly modified after 0.6 s in the short residence times (several seconds) of our experiments. Higher temperatures improve hydrogen yield in the gaseous product while CO yield decreases. Under nitrogen atmosphere, after 2 s at 950 °C, 76% (daf) of the mass of wood is recovered as gases: CO, CO 2 , H 2 , CH 4 , C 2 H 2 , C 2 H 4 and H 2 O. Tests performed under steam partial pressure showed that hydrogen production is slightly enhanced.
Fichier principal
Vignette du fichier
pyrolysisofwoodathightemperature.pdf (950.68 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01801244 , version 1 (01-06-2018)

Identifiants

Citer

Jean-Michel Commandre, H. Lahmidi, Sylvain Salvador, N. Dupassieux. Pyrolysis of wood at high temperature: The influence of experimental parameters on gaseous products. Fuel Processing Technology, 2011, 92 (5), pp.837 - 844. ⟨10.1016/j.fuproc.2010.07.009⟩. ⟨hal-01801244⟩
108 Consultations
2517 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More