Microstructure variation and hardness diminution during low cycle fatigue of 55NiCrMoV7 steel - IMT Mines Albi-Carmaux Accéder directement au contenu
Article Dans Une Revue Journal of Iron and Steel Research International Année : 2007

Microstructure variation and hardness diminution during low cycle fatigue of 55NiCrMoV7 steel

Résumé

The influence of temperature and hardness level on the cyclic behavior of 55NiCrMoV7 steel, and the microstructure variation and hardness diminution during low cycle fatigue behavior were investigated. By means of SEM and XRD, the modality of carbides and the full-width half-maximum (FWHM) of martensite (211) [M(211)] of X-ray diffraction spectrum in fatigue specimen were studied. The results showed that the cyclic stress response behavior generally showed an initial exponential softening for the first few cycles, followed by a gradual softening without cyclic softening saturation. The fatigue behavior of the steel is closely related to the hardness level. The hardness diminution and the variation of half-width M(211) are remarkably influenced by the interaction between the cyclic plastic deformation and the thermal loading when the fatigue temperature exceeds the tempering temperature of the steel.
Fichier principal
Vignette du fichier
microstructure-variation.pdf (1.17 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01715083 , version 1 (11-01-2019)

Identifiants

Citer

Zhan-Ping Zhang, Yu-Hong Qi, Denis Delagnes, Gérard Bernhart. Microstructure variation and hardness diminution during low cycle fatigue of 55NiCrMoV7 steel. Journal of Iron and Steel Research International, 2007, 14 (6), pp.68-73. ⟨10.1016/S1006-706X(07)60093-4⟩. ⟨hal-01715083⟩
67 Consultations
86 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More