Leaching of calcined phosphate ore particles with phosphoric and acetic acid solutions at 25°C : kinetic curves and related textural changes - IMT Mines Albi-Carmaux Accéder directement au contenu
Article Dans Une Revue Special Topics & Reviews in Porous Media - An International Journal Année : 2010

Leaching of calcined phosphate ore particles with phosphoric and acetic acid solutions at 25°C : kinetic curves and related textural changes

Résumé

The reactivity of calcined Tunisian phosphate ore was studied in both phosphoric and acetic solutions. Phase analysis from X-ray diffraction and IR absorption data indicate that carbonate apatite, or francolite, and fluorapatite are the main phases. However, it was observed that the calcium oxide phase, evident at the most intense peak (d=2.401Å401˚401Å;2θ= 37.42 •) and at the adsorbant band at around 700 cm −1 disappeared or were weakly defined for the solid leached in acetic medium. Nitrogen adsorption-desorption analysis shows a rising of mesopores at the surface of the leached particles and then an increase of their specific surface area, SBET. The scanning electron microscope micrographs of the particles and their size distribution show a constancy of their outer dimensions during attack.
Fichier principal
Vignette du fichier
2010.F.BenBrahim et al-HAL**.pdf (942.64 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01634508 , version 1 (23-02-2018)

Identifiants

Citer

Faouzi Ben Brahim, Arbi Mgaidi, Driss Oulahna, Mohamed El Maaoui. Leaching of calcined phosphate ore particles with phosphoric and acetic acid solutions at 25°C : kinetic curves and related textural changes. Special Topics & Reviews in Porous Media - An International Journal, 2010, 1 (3), pp.257-267. ⟨10.1615/SpecialTopicsRevPorousMedia.v1.i3.60⟩. ⟨hal-01634508⟩
159 Consultations
352 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More