Synthesis of calcium hydroxyapatite from calcium carbonate and different orthophosphate sources: A comparative study - IMT Mines Albi-Carmaux Accéder directement au contenu
Article Dans Une Revue Materials Science and Engineering: B Année : 2012

Synthesis of calcium hydroxyapatite from calcium carbonate and different orthophosphate sources: A comparative study

Résumé

The synthesis of calcium hydroxyapatite (Ca-HA) starting from calcium carbonate and different orthophosphate sources, including orthophosphoric acid, potassium, sodium and ammonium dihydrogen orthophosphates, was investigated under ambient conditions. The reaction started with calcium carbonate dissolution in an acid medium, followed by rapid precipitation of calcium cations with orthophosphate species to form calcium phosphate based particles which were in the size range of 0.4-1 mu m. These particles then agglomerated into much larger ones, up to 350 mu m in diameter (aggregates). These aggregates possessed an unstable porous structure which was responsible for the porosity of the final products. The highest specific surface area and pore volume were obtained with potassium dihydrogen orthophosphate. On the other hand, orthophosphoric acid led to the highest dissolution of calcium carbonate and the complete precipitation of orthophosphate species. Under ambient conditions, calcium phosphate based solid products of low crystallinity were formed. Different intermediates were identified and a reaction pathway proposed. (C) 2012 Elsevier B.V. All rights reserved.
Fichier principal
Vignette du fichier
synthesis-of-calcium-hydroxyapatite.pdf (1.84 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01632406 , version 1 (20-10-2018)

Identifiants

Citer

Doan Pham Minh, Nathalie Lyczko, Haroun Sebei, Ange Nzihou, Patrick Sharrock. Synthesis of calcium hydroxyapatite from calcium carbonate and different orthophosphate sources: A comparative study. Materials Science and Engineering: B, 2012, 177 (13), pp.1080-1089. ⟨10.1016/j.mseb.2012.05.007⟩. ⟨hal-01632406⟩
124 Consultations
1089 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More