Characterization of solar fuels obtained from beech wood solar pyrolysis - IMT Mines Albi-Carmaux Accéder directement au contenu
Article Dans Une Revue Fuel Année : 2017

Characterization of solar fuels obtained from beech wood solar pyrolysis

Résumé

Solar pyrolysis of biomass is a smart way to upgrade biomass and, thus, store intermittent solar energy as solar fuels (gas, bio-char and bio-oil). Distribution and energy content of gas, char and oil depend on experimental conditions. In order to determine these characteristics, experiments have been performed at temperatures of 600, 900, 1200 and 2000 degrees C, heating rate of 50 degrees C/s and argon flow rate of 6 NL/min. The gas product was analyzed by micro-GC. The char product was characterized by CHNS, whereas the oil product was subjected to CHNS, Karl-Fischer titration and GC-MS analysis. The LHVs (lower heating values) for gas, char and oil were determined from empirical equations. The gas product yield and LHV significantly increase with temperature, which is mainly due to more H-2 and CO formation by the enhanced secondary tar reactions. The char and oil characteristics highly depend on the temperature. Their high energy contents show that the obtained char and oil can be utilized as valuable solid and liquid fuels. The biomass energy upgrading due to solar processing is discussed. At optimum temperature 900 degrees C, it ranges from 38% to 53% accounting for the uncertainty of bio-oil water content.
Fichier principal
Vignette du fichier
Zeng-characterizationofsolarfuel-2017.pdf (1.73 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01619246 , version 1 (04-05-2018)

Identifiants

Citer

Kuo Zeng, Daniel Gauthier, Doan Pham Minh, Elsa Weiss-Hortala, Ange Nzihou, et al.. Characterization of solar fuels obtained from beech wood solar pyrolysis. Fuel, 2017, 188, p. 285-293. ⟨10.1016/j.fuel.2016.10.036⟩. ⟨hal-01619246⟩
136 Consultations
693 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More